28-12-2013, 12:39 PM
Would you go for the side exit design? You can get directional tee joints, lateral tees I think there called. 3 of them, a long radius 90 and the flange and your sorted. I would shotblast the inside once its welded or acid dip it. Out of interest where is your manifold cracking and have you got pics of it?